687.22 Jowapur® 1K PUR AdhesiveID68722
Flüssiger universeller 1K PUR D4-Montageklebstoff von Jowat® für diverse Werkstoffe und Oberflächen mit mittlerer Offener Zeit.

Prix sans Livraison, hors taxe TVA et COV si applicable.


Adhesive for soft wood species, also with high moisture content, for bonding mineral aggregate panels, fiberboard and PUR foam, compound elements and timber which is used for instance for the manufacture of wooden window frames and garden furniture. Bonded larch wood is to be protected against direct contact with water.

Characteristics / Directions for Use:

Free of solvents and formaldehyde. Good adhesion to many substrates. Moisture-curing. High strength data. Meets the requirements of D4 according for to the EN 204/205. Heat resistance level according to the Watt ‘91 >7 N/mm² at 80 °C. Standard application of the adhesive is one-sided by spatula or roller. In case of non-absorbent substrates and wood with moisture content below 8 %, the adhesive film or the materials to be bonded are to be fogged. Please take care during pressing to prevent the press from gluing shut. Coat the press with a suitable Jowat® release agent for PU adhesives. We recommend using release paper. Our Application Technology Department and our Application Specialists will provide technical data to assist you in your choice of an appropriate product for your requirements. Please observe the information in the section “Remarks.” General bonding requirements The properties (e.g. surface tension, plasticizer content…) and the conditioning of the substrates, as well as the processing conditions (e.g. ambient temperature, humidity…) will influence the processes of joining and bonding. Customer tests under consideration of everyday production conditions are therefore absolutely necessary to define stable process parameters and to ensure that the product is fit for purpose. For best bonding results, the materials to be bonded should be free of dust, oil, and grease, and be dry. Ideally, the minimum temperature should be at 18 °C. Avoid draft.


Before curing, the prepolymer can be cleaned with a dry or a solvent-soaked rag for instance using Jowat® Thinner 401.30 or Jowat® PUR Cleaner 402.38. After curing, only mechanical removal (e.g. emery paper).


The product should remain stored in properly closed original containers, cool and dry (15 – 25 °C). Do not transport at temperatures below +5 °C. For best-before date, please see container label. After the elapse of the best-before date, it is essential that you again verify that the product is fit for your intended application.


Information about packaging types and units is available upon request.


For further information concerning safety, handling, transport and disposal, please refer to the safety data sheet. The information on this data sheet is based on test results from our laboratories as well as on reported experience gained in the field by our customers. It can, however, not cover all parameters for each specific application and is therefore not binding upon Jowat, nor should it be relied upon in lieu of your own required testing. The information given in this leaflet does not represent a performance guarantee. Unless otherwise agreed with our customers, the values stated in the section “Specification” shall be regarded as the finally agreed upon product properties. No liability may be derived from the information contained herein nor from the information provided by our free technical advisory service.

Please refer to the "Download" tab for the safety data sheet.

Base Polyurethan (PU/PUR)
Viscosity 10.200 ± 2.500 mPas (Brookfield)
Processing temperature > 10 °C
Density at +20 °C [g/cm³] ca. 1,1 g/cm³ (Jowat Prüfmethode)
Appearance of the glue film brown transparent
Viscosity at 20 °C [mPas] 10.200 ± 2.500
VOC content (Swiss) 0,00%
Open time at 20 °C / 50% RH [min] 16-20 minutes
Solids content 99,0 ± 1,0
Minimum pressing time at 20 °C (Jowat test method) in minutes approx. 60 minutes
Stress group D4 + Watt '91
Foaming strong