148.20 Jowacoll® Foil AdhesiveID14820
Schnellabbindender wärmebeständiger Kaltleim von Jowat® für die Flächenklebung mit Kunststofffolien oder zum manuellen Kleben von Kanten.

Prix sans Livraison, hors taxe TVA et COV si applicable.


Dispersion of vinyl acetate copolymer for laminating PVC foils and decor paper to particleboard and hardboard as well as to plywood, using roller laminators and wrapping machines. Can also be used for manual edgebanding. If individual applications demand an increased water resistance, it is possible to add 7 % Jowat® Crosslinker 195.60. In this case a pot life limitation of max. 2 hours must be observed. When foils are bonded, using crosslinkers may lead to a loss of adhesion. This requires preliminary testing for the specific case.

Characteristics / Directions for Use:

Good mechanical processing characteristics, fast setting, good heat resistance. We recommend that all materials coming into contact with the glue are made of high-quality stainless steel (German standard V2A according to DIN EN 10027 – W‑No. 1.4301 or better) or of inert plastics, e.g. Teflon, PP, polyamide. Avoid contact with other metals like zinc, brass, copper or aluminium. For more information, contact the equipment manufacturer or our technical service. The adhesive is applied one-sided to the base boards (lamination) or to the wrapping material. During storage, the viscosity of the product may increase due to chemical reactions of the ingredients that cannot be influenced. Higher storage temperatures promote that increase in viscosity. We therefore recommend using a suitable tool to stir the product before use. This reduces the viscosity. Our Application Technology Department and our Application Specialists will provide technical data to assist you in your choice of an appropriate product for your requirements. Please observe the information in the section “Remarks.”


Machines and equipment may be cleaned after use with warm or cold water, using Jowat® Cleaner Concentrate 192.40.


The product should remain stored in properly closed original containers, dry and cool (15 – 25 °C). For best-before date, please see container label. After the elapse of the best-before date, it is essential that you again verify that the product is fit for your intended application. Protect from frost.


Information about packaging types and units is available upon request.


For further information concerning safety, handling, transport and disposal, please refer to the safety data sheet. The information on this data sheet is based on test results from our laboratories as well as on reported experience gained in the field by our customers. It can, however, not cover all parameters for each specific application and is therefore not binding upon Jowat, nor should it be relied upon in lieu of your own required testing. The information given in this leaflet does not represent a performance guarantee. Unless otherwise agreed with our customers, the values stated in the section “Specification” shall be regarded as the finally agreed upon product properties. No liability may be derived from the information contained herein nor from the information provided by our free technical advisory service.

For the complete technical data sheet click here

Please refer to the "Download" tab for the safety data sheet.

Base Copolymer
Viscosity bei 20 °C: 20.000 ± 6.000 mPas (Brookfield RV, Spindel 5, 20 UPM)
Processing temperature min. 15 °C
Density at +20 °C [g/cm³] at 20 °C: ca. 1,35 ± 0,02 g/cm³
Application quantity approx. 95 ± 25 g/m²
Viscosity at 20 °C [mPas] 19.500 ± 6.500
VOC content (Swiss) 0,04%
Open time at 20 °C / 50% RH [min] bei Raumtemperatur: ca. 3 Minuten (Jowat Prüfmethode)
Solids content approx. 70 ± 3 %
pH value at 20 °C: 7,5 ± 1