685.17 Jowapur® 1K PUR-prepolymerID68517
Pastöser universeller 1K PUR D4-Montageklebstoff von Jowat® für diverse Werkstoffe und Oberflächen mit kurzer offener Zeit.
  • Universeller Klebstoff für Montageanwendungen
  • Sehr gute Haftung zu vielen Oberflächen
  • Gering schäumend
  • Lösemittel- und formaldehydfrei
  • Sehr hohe Festigkeiten
  • Schulungspflichtiges Produkt – Bitte Produktdetails beachten
Quantity Price each
1-11 € 11,50
12+ € 10,35
excl. VAT plus Shipping
low stock


Adhesive for bonding soft wood species, windows, doors, construction elements, water-resistant particleboard, foam and insulating materials made of concrete, cork and coated cork, ceramic and laminate tiles, stone and many other substrates. Bonded larch is to be protected against direct contact with water.

Characteristics / Directions for Use:

Free of solvents and formaldehyde. Good adhesion to many substrates. Moisture-curing. Joint-filling. High strength level. Meets durability class D4 following EN 204/205. Standard application of the adhesive is by one-sided application in bead form from the cartridge, spread with spatula as required In case of non-absorbent substrates and wood with moisture content below 8 %, the adhesive film or the materials to be bonded are to be fogged. Please take care during pressing to prevent the press from gluing shut. Coat the press with a suitable Jowat® release agent for PU adhesives. We recommend using release paper. Our Application Technology Department and our Application Specialists will provide technical data to assist you in your choice of an appropriate product for your requirements. Please observe the information in the section “Remarks”. General bonding requirements The properties (e.g. surface tension, plasticiser content…) and the conditioning of the substrates, as well as the processing conditions (e.g. ambient temperature, humidity…) will influence the processes of joining and bonding. Customer tests under consideration of everyday production conditions are therefore absolutely necessary to define stable process parameters and to ensure that the product is fit for purpose. For best bonding results, the materials to be bonded should be free of dust, oil, and grease, and be dry. Ideally, the minimum temperature should be at 18 °C. Avoid draught.


Before curing the prepolymer can be cleaned with a solvent-soaked rag for instance using Jowat® Thinner 401.30 or with Jowat® PUR Cleaner 402.38 after curing only mechanical removal (emery paper).


The product should remain stored in properly closed original containers, dry and cool (15 – 25 °C). Do not transport at temperatures below +5 °C. For best-before date, please see container label. After the elapse of the best-before date, it is essential that you again verify that the product is fit for your intended application.


Information about packaging types and units is available upon request.


For further information concerning safety, handling, transport and disposal, please refer to the Safety Data Sheet. The information on this data sheet is based on test results from our laboratories as well as on reported experience gained in the field by our customers. It can, however, not cover all parameters for each specific application and is therefore not binding upon Jowat, nor should it be relied upon in lieu of your own required testing. The information given in this leaflet does not represent a performance guarantee. Unless otherwise agreed with our customers, the values stated in the section “Specification” shall be regarded as the finally agreed upon product properties. No liability may be derived from the information contained herein nor from the information provided by our free technical advisory service.

For the complete technical data sheet click here

Please refer to the "Download" tab for the safety data sheet.

Base Polyurethan (PU/PUR)
Viscosity bei 23 °C: pastös
Processing temperature min. 10 °C
Density at +20 °C [g/cm³] bei +20 °C [g/cm³]: ca. 1,20 ± 0,05 (Jowat Prüfmethode)
Viscosity at 20 °C [mPas] 1,20 ± 0,05 g/cm³ (Jowat Prüfmethode)
Open time at 20 °C / 50% RH [min] 12 ± 3 Minuten (Jowat Prüfmethode)
Solids content 95 ± 5 % (Jowat Prüfmethode)
Minimum pressing time at 20 °C (Jowat test method) in minutes ca. 50,5 ± 5,5 Minuten bei 20 °C; ca. 17,5 ± 2,5 Minuten bei 40 °C
Stress group D4 + Watt '91
Foaming gering

Bevat: difenylmethaandiisocyanaat, isomeren en homologen, methyleendifenyldiisocyanaat.

Veroorzaakt huidirritatie. Veroorzaakt ernstige oogirritatie. Kan bij inademing allergie- of astmasymptomen of ademhalingsmoeilijkheden veroorzaken. Kan een allergische huidreactie veroorzaken. Verdacht van het veroorzaken van kanker. Kan irritatie van de luchtwegen veroorzaken. Kan schade aan organen veroorzaken bij langdurige of herhaalde blootstelling. Bevat isocyanaten. Kan een allergische reactie veroorzaken. ### Per 24 augustus 2023 moet voor industrieel of beroepsmatig gebruik een passende opleiding zijn voltooid. ###
Stof/rook/gas/nevel/damp/spuitnevel niet inademen. Beschermende handschoenen/beschermende kleding/oog­bescherming/gelaatsbescherming dragen. BIJ CONTACT MET DE OGEN: voorzichtig afspoelen met water gedurende een aantal minuten; contactlenzen verwijderen, indien mogelijk; blijven spoelen. Bij ademhalingssymptomen: Een ANTIGIFCENTRUM/arts raadplegen. Op een goed geventileerde plaats bewaren. In goed gesloten verpakking bewaren. Inhoud/verpakking afvoeren naar een goedgekeurde afvalverwijdering of recycling in overeenstemming met de nationale regelgeving.